Product Details:
|
| Length: | 3mm ~ 2000mm | Product Name: | Corrosion Resistance Hardness Wear 99% Alumina Ceramic Plate |
|---|---|---|---|
| Material: | Alumina Ceramic | Application: | Industrial Ceramic |
| Packaging Details: | Box, Carton, Wooden, Bag Etc. Customized Package | Water Absorption: | 0% |
| Electrical Insulation: | Excellent | Density: | 3.9g/cm3 |
| High Light: | 99% alumina ceramic sheet,HRA80-90 alumina ceramic sheet,ODM alumina ceramic sheet |
||
Corrosion Resistance Hardness Wear 99% Alumina Ceramic plate
Description:
Alumina industrial ceramic wear liner / special ceramic plates of 92 al2o3 are sintered on high temperature of more than 1530 , with high-purity ultra-fine alumina powder as raw material according to optimized formulation design. They are usually installed uopn the wear areas of some material conveying equipments, coal preparation equipments and so on to be used as the material contact surface to bear the following abrasion and impact.
Technical Parameters:
| Test item/Unit | Numerical Value | Test item/Unit | Numerical | ||||
| Product Material | Alumina | Zirconia | Product Material | Alumina | Zirconia | ||
| Component Content % | ≥99% | ≥95% | ≥90% | Volume Resistance MM | >1012 | >1012 | >1012 |
| Sintering Temp ℃ | 1780-1800 | 1650-1680 | 1550-2600 | Bending Strength Mpa | 400 | 320 | 1100 |
| Specific Gravity g/cm3 | ≥3.8 | ≥3.6 | >6 | Thermal Expansion Coefficient'10' | 6.8-8.0 | 6.2-8.5 | 6.9-10 |
| Breakdown Voltage Strength kv/mm |
15 | 15 | 15 | Roughness um | ≤0.8 | ≤0.8 | ≤0.8 |
| Bibulous Rate% | <0.01 | <0.01 | <0.01 | Mirror Polished Ra | ≤0.05 | ≤0.1 | ≤0.05 |
| Anti Pressure Mpa | 3700Mpa | 2400Mpa | 5000Mpa | Thermal Conductivity W/m.k | 25 | 20 | 25 |
| Hardness Hra | ≥88 | ≥82 | ≥88 | Temperature Resistance ℃ | 1700 | 1600 | 1800 |
Advantages:
1. High hardness: The hardness of rockwell is hRA80-90, which is second only to diamond and far more than wear-resistant steel and stainless steel.
2. Excellent wear resistance: Wear resistance is 266 times that of manganese steel and 171.5 times that of high-chromium cast iron.According to our customer tracking survey over the past ten years, the service life of the equipment can be extended at least ten times under the same working condition.
3. Light weight: Its density is 3.5g/cm3, only half that of steel, which can greatly reduce equipment load.
Application:
1. Ceramics, mines and other grinding equipment lining.
2· Material thansfer equipment.
3· inside and outside surface of powder separating equipment on iron and steel works.
4· Thermal and power plants.