Product Details:
|
| Inner Diameter: | 210mm / Customized | Outer Diameter: | 242mm / Customzied |
|---|---|---|---|
| Height: | 120mm | Advantage: | Long Working Life |
| Item: | Zirconia Ceramic Wheel Used For For Crushing Equipment | Density: | 6.0g/cm3 |
| Bibulous Rate: | <0.01% | Surface: | Smooth |
| Heat Expansion Rate (10-6K-1): | 10 | Color: | White |
| High Light: | Zirconia Ceramic Wheel,Smooth Zirconia Ceramic Wheel,Crushing Equipment Ceramic Wheel |
||
Zirconia Ceramic wheel used for for crushing equipment
Description:
Zirconia Ceramic hierarchical wheel working principle: Under the action of fan pumping force, the material moves to the classification zone along with the updraft. Under the action of the powerful centrifugal force generated by the high-speed rotating classification turbine, the coarse and fine materials are separated. The fine particles that meet the requirements of strength are collected by the cyclone separator and dust collector through the classification theory, and the coarse particles are dropped to the grinding zone to continue grinding.
The motor drives the ceramic grading wheel to rotate at high speed in the grading shell (the speed can be adjusted arbitrarily), forming a strong centrifugal force in the classifier. The air powder mixture into the classifier first enters the inside of the classifier wheel. Under the action of centrifugal force, the large or heavy particles are subject to centrifugal pressure, so they are thrown to the periphery of the classifier wheel to the side wall of the classifier, and are no longer affected by centrifugal force, and naturally fall into the main grinding machine to continue crushing or fall into the discharge port for collection; Small or light materials by centrifugal force is small, hovering in the classification wheel, induced by the influence of the induced draft fan is brought to a high point, along the pipeline moving to the next component is classified or collected.
Principal characteristic of Zirconia Ceramic hierarchical wheel used for for crushing equipment:
1. High density.
2. High fracture toughness .
3. High hardness High Mechanical Strength.
4. Low thermal conductivity Excellent insulation .
5. Good Wear resistance.
6. Resistant to Corrosion and Chemical Attack.
7. Extreme Temperature Stability.
8. Outstanding Electrical and Electronic Properties.
Application of Zirconia Ceramic hierarchical wheel used for for crushing equipment:
Ultrafine grinding equipment, fine chemical industry, electronic paste, semiconductor, new energy, nano new materials, medical instruments, precision casting, structural ceramics, refractory materials, electronic communications, sensitive ceramics, petrochemical industry, aerospace, machinery manufacturing, optical fiber connector, battery materials and other high-precision end fields.
Technical Parameters:
| Items | unit | Typical Values |
| Composition | (wt%) | 94.8%ZrO2+5.2%Y2O3(wt%) |
| Color | - | White |
| Density | g/cm3 | 6.03 |
| Water absorption | ％ | 0 |
| flexure strength | MPa | 1250 |
| HV hardness | GPa | 1300 |
| Modulus of Elasticity | GPa | 210 |
| Poisson's ratio | - | 0.31 |
| fracture toughness | MPa m1/2 | 8-10 |
| thermal expansivity | [normal temperature～400℃] x10-6 | 10.3 |
| Thermal conductivity | W/(m.K) | 3 |
| nitric acid(90%) | weight loss | 0 |
| sulfuric acid(95%) | 0.03 | |
| sodium hydroxide(30%) | 0.07 |
|
Performance |
Unit |
Typical value |
|
Density |
g/cm3 |
>6.0 |
|
HV Hardness |
Kg/mm2 |
>1300 |
|
Compressive Strength |
MPa |
5500 |
|
Flexural Strength |
MPa |
1250 |
|
Modulus of Elasticity |
Gpa |
200 |
|
Thermal Conductivity |
W/(m.k) |
3(20-400℃) |
|
Thermal Expansivity Cofficient |
10^-6K^-1 |
10 |
|
Facture Toughness |
Mpa.m0.5 |
8 |
|
Grain Size |
um | 0.5 |