Product Details:
|
| Material: | Zirconia | Flexural Strength: | 1250 MPa |
|---|---|---|---|
| Advantage: | Long Working Life | Item: | Laboratory Special Wear Resistant Zirconia Ball Grinding Tank |
| Density: | 6.0g/cm3 | Bibulous Rate: | <0.01% |
| Modulus Of Elasticity: | 210Mpa | Heat Expansion Rate (10-6K-1): | 10 |
| Specification: | 50ML-1L | Color: | White |
| High Light: | Zirconia Ball Grinding Tank,Grinding Tank Zirconia Ceramic Parts,Zirconia Ceramic Parts Wear Resistant |
||
Laboratory special wear resistant zirconia ball grinding tank
Description:
Zirconia material has high hardness, high strength, high toughness, high properties and chemical corrosion resistance and other excellent physical and chemical properties, zirconia has been used in ceramics, refractories, machinery, electronics, optics, aerospace, biology, chemistry and other fields. This is your zirconia ball mill tank with a hardness of 12.3(GPa), volume density of 6(g.CM-3), and consumption resistance of 0.48(PPM/HRS). Smooth appearance, compact and high purity, with high hardness, impact resistance, strong acid and alkali resistance, resistance to various solvents, high, no pollution products, long service life, grinding. It can be used in precious metals, electronic ceramics, magnetic materials, color coatings and other industries.
Principal characteristic of Ceramic tank Zirconia ball mill tank Alumina ball mill tank high temperature tank:
1 High wall finish, not easy to stick material.
2. Strong oxidation resistance, acid and alkali resistance.
3. Excellent corrosion resistance
4. Good intergranular corrosion resistance
5. High temperature resistance is also better.
6. High wear resistance and long service life.
7. High grinding efficiency.
Application of Ceramic tank Zirconia ball mill tank Alumina ball mill tank high temperature tank:
Ultrafine grinding equipment, fine chemical industry, electronic paste, semiconductor, new energy, nano new materials, medical instruments, precision casting, structural ceramics, refractory materials, electronic communications, sensitive ceramics, petrochemical industry, aerospace, machinery manufacturing, optical fiber connector, battery materials and other high-precision end fields.
Technical Parameters:
| Specification | Outer diameter | inner diameter | Bottom diameter | Height | Cover thickness |
| 50ML | 64 | 50 | 64 | 56 | 12 |
| 100ML | 74 | 60 | 64 | 68 | 12 |
| 250ML | 94 | 80 | 89.5 | 88 | 13 |
| 500ML | 103 | 89 | 89.5 | 100 | 13 |
| 1L | 130 | 114 | 119.5 | 118 | 13 |
| TIPS:The size list is for reference only, the above is the standard size of conventional products,specialspecifications can be customized . | |||||
| Item | unit | Typical Values |
| Composition | (wt%) | 94.8%ZrO2+5.2%Y2O3(wt%) |
| Color | - | White |
| Density | g/cm3 | 6.03 |
| Water absorption | ％ | 0 |
| flexure strength | MPa | 1250 |
| HV hardness | GPa | 1300 |
| Modulus of Elasticity | GPa | 210 |
| Poisson's ratio | - | 0.31 |
| fracture toughness | MPa m1/2 | 8-10 |
| thermal expansivity | [normal temperature～400℃] x10-6 | 10.3 |
| Thermal conductivity | W/(m.K) | 3 |
| nitric acid(90%) | weight loss | 0 |
| sulfuric acid(95%) | 0.03 | |
| sodium hydroxide(30%) | 0.07 |
Advantages:
1). Excellent electrical insulation;
2). High hardness;
3). Relatively low strength and fracture toughness;
4). Resistance to wear and corrosive;
5). Excellent thermal stability;
6). Resistance to high temperatures;
7). High electrical resistivity;
8). Good chemical stability and resistance.