Product Details:
|
| Material: | Zirconia | Flexural Strength: | 1250 MPa |
|---|---|---|---|
| Advantage: | Long Working Life | Item: | High Hardness Pollution-free Zirconia Ceramic Mortar |
| Density: | 6.0g/cm3 | Bibulous Rate: | <0.01% |
| Modulus Of Elasticity: | 210Mpa | Heat Expansion Rate (10-6K-1): | 10 |
| Specification: | 50ML-1L | Color: | White |
| High Light: | Zirconium Oxide Mortar,High Hardness Zirconia Mortar,Pollution Free Zirconia Mortar |
||
High hardness pollution-free zirconia ceramic mortar
Description:
Zirconia mortar is mainly used for grinding and analyzing a small number of samples in the laboratory. It is used for grinding solid substances or mixing powdered solids.
Application method:
Wash and dry the mortar, and then put the grinding material into the bowl. First cover the mouth of the bowl with the left hand, and gently crush the coarse material with the right hand glass pestle, and then grind. Until the fineness is reached, the grinding material is poured out from the mouth and continues to grind after sifting the coarse grain. If you want to make a paste, you can also use a mortar, the method is the same as above, but because of the large contact surface of fine particles after grinding, the dissolution speed is increased, after grinding, the yan distillate water is directly added in the bowl, to be adjusted into a paste by the tip of the tip, and finally washed with distilled water, the washing liquid is also poured into the container.
Application of Advanced grinding, smooth, abrasion resistant, high hardness zirconia mortar:
Ultrafine grinding equipment, fine chemical industry, electronic paste, semiconductor, new energy, nano new materials, medical instruments, precision casting, structural ceramics, refractory materials, electronic communications, sensitive ceramics.
Technical Parameters:
| Item | unit | Typical Values |
| Composition | (wt%) | 94.8%ZrO2+5.2%Y2O3(wt%) |
| Color | - | White |
| Density | g/cm3 | 6.03 |
| Water absorption | ％ | 0 |
| flexure strength | MPa | 1250 |
| HV hardness | GPa | 1300 |
| Modulus of Elasticity | GPa | 210 |
| Poisson's ratio | - | 0.31 |
| fracture toughness | MPa m1/2 | 8-10 |
| thermal expansivity | [normal temperature～400℃] x10-6 | 10.3 |
| Thermal conductivity | W/(m.K) | 3 |
| nitric acid(90%) | weight loss | 0 |
| sulfuric acid(95%) | 0.03 | |
| sodium hydroxide(30%) | 0.07 |
Advantages:
1. The product has no crack, no impurity and strong resistance to wear.
2. The product has high gloss and strong corrosion resistance, and can be used in acid grinding materials.
3. High purity and hardness, which meet the quality and technical standards.
Advisories and Precautions:
1. In the process of use, special care should be taken to avoid grinding substances with excessive hardness and contact with hydrofluoric acid.
2. The mortar should not be heated, and should not be dried in the electric oven.
3.Washing mortar, should be washed with water first, acid corrosion resistant mortar can be washed with dilute hydrochloric acid. When there is a hard-to-wash substance attached to the mortar, put a small amount of salt into it and grind it before washing it.